Title: Evaluación de la estabilidad del color y dureza de las resinas compuestas sometidas a clorhexidina
Author: Arango-Santander, Santiago
Avilez-Causil, Aura
Perez-Ruiz, Laura
Ramirez-Galeano, Mariana
Freitas, Sidónio
Email autor: santiago.arango@campusucc.edu.co
aura.avilezc@campusucc.edu.co
laura.perezru@campusucc.edu.co
mariana.ramirezg@campusucc.edu.co
sidonio.freitas@campusucc.edu.co
metadata.dc.description.cvlac: https://scienti.colciencias.gov.co/cvlac/EnRecursoHumano/inicio.do
Issue Date: 23-May-2019
Advisor / Validator: Arango-Santander, Santiago
Keywords: clorhexidina
color
dureza
resinas
Resume: Objetivos: Este estudio tuvo como objetivo evaluar la estabilidad del color y de la dureza de las resinas compuestas nano híbridas sometidas a clorhexidina. Materiales y Métodos: estudio experimental in-vitro. Para la muestra se fabricaron 30 discos de resina nanohibrida de 1.0 cm de diámetro y 1.0 mm de espesor. El grupo experimental fue sometido a enjuagues de clorhexidina al 0.12% con agitación durante 2 minutos por un periodo de 14 días. Se obtuvieron muestras en los días 0, 7 y 14. Las muestras control se mantuvieron en lubricante salival simulando propiedades orales como humedad y temperatura. La recolección de la información se llevó a cabo con espectrofotometría de reflexión y dureza Vickers evaluadas sobre cada muestra. En todos los análisis se tomó un valor de significación estadística p<0,05 realizado mediante el paquete estadístico IBM SPSS ® 25. Resultados: Para el color, los resultados en el grupo control mostraron un valor de delta de E de 1,09 ± 0,26 y el grupo experimental un valor de 1,58 ± 1,22. Esta diferencia no fue significativo estadisticamente con un valor de p=0,12. Con respecto a la dureza, el grupo control arrojó un valor de HV de 81.25 ± 3.66 y el grupo experimental un valor de 86.80 ± 6.76. La diferencia en la disminución de la dureza de las muestras sometidas a clorhexidina fue significativo significativamente con un valor p=0,026. Conclusiones: El uso de clorhexidina al 0.12% durante 14 días produjo disminución significativa estadísticamente de la dureza, pero no se observaron cambios en el color con el enjuague utilizado.
Abstract: Objective: the main objective was to assess color stability and surface hardness of nano hybrid dental composites after exposure to chlorhexidine. Materials and methods: for this in –vitro experimental study, 30 discs (1.0cm in diameter and 1.0mm in thickness) were manufactured using a nano hybrid dental composite. The experimental group was exposed to a 0.12% chlorhexidine solution under constant agitation for 2 minutes during a period of 14 days. Samples from days 0, 7 and 14 were collected and evaluated. The control group was kept in salivary substitute at 37°C to simulate oral humidity and temperature. Color stability was assessed via spectrophotometry and surface hardness through micro indentation using the Vickers test. Statistical significance was established at p<0.05. Results: for color stability, E delta (ΔE) values of 1.09 ± 0.26 for the control group and 1.58 ± 1.22 for the experimental group were obtained. The difference was not statistically significant. For surface hardness, values for the control group of 81.25 ± 3.66 HV and 86.60 ± 6.76 HV for the experimental group were found. The reduction in hardness for the experimental group was statistically significant. Conclusions: a reduction in surface hardness after exposure to a 0.12% chlorhexidine solution was found. No changes in color were observed with this particular solution.
Program: Odontología
Headquarters: Medellín
Type: Trabajos de grado - Pregrado
Citation: Arango-Santander, S., Avilez-Causil, A., Perez-Ruiz, L.C., Ramirez-Galeano, M. y Freitas, S. (2019). Evaluación de la estabilidad del color y dureza de las resinas compuestas sometidas a clorhexidina. (Tesis de pregrado). Recuperado de:
Appears in Collections:Odontología



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.