Title: Efecto del pH en la resistencia a la tracción de la sutura poliglactina 910 en diferentes tiempos de exposición: estudio in vitro
Author: Chavarriaga Tamayo, David
Grajales Fernández, Natalia
Torres Arango, Julián Andrés
Email autor: david.chavarriagat@campusucc.edu.co
natalia.grajalesf@campusucc.edu.co
julian.torresa@campusucc.edu.co
Issue Date: 6-Dec-2018
Advisor / Validator: Leon Garcia, Alejandro
Erira Tupaz, Alveiro
Keywords: Resistencia
Tracción
pH
Tiempo
Sutura
Poliglactina910
Resume: La deficiencia en la resistencia del material de sutura lleva a una mala adaptación de los colgajos quirúrgicos, es importante conocer que el material de sutura puede verse afectado por diferentes factores entre ellos el pH. El objetivo fue evaluar el efecto del pH sobre la resistencia a la tracción de la sutura poliglactina 910ETHICON® de calibre 5.0 en diferentes tiempos. Materiales y métodos: se realizó un estudio experimental in vitro, con sutura poliglactina 910 ETHICON® 5.0, con una muestra de 51 tramos de 8 cm. Las variables fueron resistencia a la tracción, pH y tiempo. Cada tramo fue sumergido en pH diferentes (3.0, 5.0, 7.0 y 8.0) y en diferentes tiempos (15min, 2h, 72h y 168h), posteriormente fueron sometidos a una fuerza unidireccional de tracción medidos en N/cm2 en un dinamómetro IMADA DS2-50N previamente calibrado, como control negativo se utilizaron tres tramos de sutura sin exposición a pH y en tiempo cero, los datos fueron analizados mediante medidas de tendencia central, se realizó un análisis estadístico multivariado con el software R versión 3.4.4 con la función Profile Analysis by Group. Resultados: La resistencia del grupo control (sin aplicar ninguna variable) fue en promedio de 9.2 N/cm2. Cumplidos los 15 minutos de exposición en sustancias buffer, la resistencia a la tracción fue en promedio de 8,35 N/cm2 en pH 3, 7.20 N/cm2 en pH 5, 7.67 N/cm2 en pH 7 y 8.17 N/cm2 en pH 8. Después de 2 horas tuvo una media de 7.10 N/cm2 en pH 3, 7.06 N/cm2 en pH 5, 6.46 N en pH7 y 5.07 N/cm2 en pH 8. A las 72 horas fue de 5.67 N/cm2 en pH 3, 6.42 N/cm2 en pH 5, 6.40 N/cm2 en pH 7 y 5.76 N/cm2 en pH 8 y a 168 horas el promedio de resistencia fue de 2.49 N/cm2 en pH 3, 3.96 N/cm2 en pH 5, 4.03 N/cm2 en pH 7 y 3.79 N/cm2 en pH 8. Conclusiones: La resistencia a la tracción de la poliglactina 910 ETHICHON ® 5/0 disminuye a través del tiempo tanto en pH ácidos como alcalinos, siendo el pH 3 a las 168 horas el que genero mayor pérdida de la resistencia con un promedio 2,49N/cm2.
Abstract: The deficiency in the resistance of the suture material leads to a poor adaptation of the surgical flaps, it is important to know that the suture material can be affected by different factors including the pH. The objective was to evaluate the effect of pH on the tensile strength of the 5.0 caliber polyglactin 910ETHICON® suture at different times. Materials and methods: an in vitro experimental study was carried out, with polyethylene 910 ETHICON® 5.0 suture, with a sample of 51 sections of 8 cm. The variables were tensile strength, pH and time. Each section was immersed in different pH (3.0, 5.0, 7.0 and 8.0) and at different times (15min, 2h, 72h and 168h), later they were subjected to a unidirectional tensile force measured in N / cm2 on an IMADA DS2-dynamometer. 50N previously calibrated, as a negative control, three suture stretches without exposure to pH and zero time were used, the data were analyzed by means of central tendency measurements, a multivariate statistical analysis was performed with software R version 3.4.4 with the Profile function Analysis by Group. Results: The resistance of the control group (without applying any variable) was on average 9.2 N / cm2. After 15 minutes of exposure in buffer substances, the tensile strength was on average 8.35 N / cm2 at pH 3, 7.20 N / cm2 at pH 5, 7.67 N / cm2 at pH 7 and 8.17 N / cm2 at pH 8. After 2 hours it had an average of 7.10 N / cm2 at pH 3, 7.06 N / cm2 at pH 5, 6.46 N at pH7 and 5.07 N / cm2 at pH 8. At 72 hours it was 5.67 N / cm2 at pH 3, 6.42 N / cm2 at pH 5, 6.40 N / cm2 at pH 7 and 5.76 N / cm2 at pH 8 and at 168 hours the average resistance was 2.49 N / cm2 at pH 3. 3.96 N / cm2 at pH 5, 4.03 N / cm2 at pH 7 and 3.79 N / cm2 at pH 8. Conclusions: The tensile strength of polyglactin 910 ETHICHON ® 5/0 decreases over time in both acidic and alkaline pHs, being pH 3 at 168 hours the one that generated the greatest loss of resistance with an average of 2.49 N / cm2.
Table Of Contents: Introducción. -- 1.Contexto de la investigación. -- 1.1.Planteamiento del problema. -- 1.2.Justificación. -- 1.3.Marco teórico y referencial. -- 1.3.1.Marco teórico. -- 1.3.2.Marco referencial. -- 1.4.Objetivos. -- 1.4.1.General. -- 1.4.2.Específicos. -- 2.Método. -- 2.1.Tipo de estudio. -- 2.2.Población. -- 2.3.Criterios de selección. -- 2.3.1.Criterios de inclusión. -- 2.3.2.Criterios de exclusión. -- 2.4.Muestra. -- 2.5.Operacionalización de variables. -- 2.6.Hipótesis. -- 2.7.Procedimiento. -- 2.8.Análisis estadístico. -- 2.9.Aspectos éticos. -- 3.Resultados. -- 4.Discusión. -- 5.Conclusiones. -- Bibliografía. -- Anexos.
Program: Especialización en Periodoncia y Oseointegración
Headquarters: Bogotá
Publisher: Universidad Cooperativa de Colombia, Facultad de Ciencias de la Salud, Odontología, Programa Periodoncia y Oseointegración, Bogotá
Citation: Chavarriaga Tamallo, D., Grajales Fernández, N. y Torres Arango, J. A. (2018). Efecto del pH sobre la resistencia a la tracción de la sutura poliglactina 910 en diferentes tiempos. Estudio in vitro (tesis de posgrado). Recuperado de: http://repository.ucc.edu.co
Appears in Collections:Odontología

Files in This Item:
File Description SizeFormat 
2018_Ph_Resistencia_Sutura_Poliglactina_LicenciaUso.pdfPublicación en la web399.91 kBAdobe PDFView/Open Request a copy
2018_Ph_Resistencia_Sutura_Poliglactina.pdfTrabajo final1.01 MBAdobe PDFView/Open
2018_Ph_Resistencia_Sutura_Poliglactina_artículo.pdfArtículo712.97 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.