Title: Efectos sobre microdureza y grado de conversión de dos tipos de resinas sometidas a tratamientos de pospolimerización
Effects on Micro-Hardness and Conversion Level of Two Types of Resins Undergoing Post-Polymerization Treatments
Efeitos sobre microdureza e grau de conversão de dois tipos de resinas submetidas a tratamentos de pós-polimerização
Author: Lapesqueur, Melissa
Surriaga, Patricia
Masache, María Elena
Vásquez, Berenice
Peña, Mauricio
Mongruel Gómes, Osnara María
Domínguez, John Alexis
Keywords: grado de conversión; microdureza: resinas compuestas.
degree of conversion; micro-hardness; composite resins
grau de conversão; microdureza; resinas compostas
Description: Objetivo:evaluar la microdureza y el grado de conversión después de diferentes técnicas poscurado en dos tipos de resinas compuestas. Materiales y métodos: se realizaron 36 cuerpos de prueba con 12 mm de diámetro y 4 mm de altura, con dos resinas: Filtek z350 y Ena Miscerium. Después de la confec-ción, los cuerpos de prueba se llevaron al microduremetro y a espectroscopia de infrarrojo, y fueron sometidos a cuatro procesos de pospolimerización: agua en ebullición, microonda, calor seco, autoclave y horno gradia. Resultados: se hizo análisis estadístico por medio de Anova de dos factores con postest Tukey por resina evaluada, se presentan media y desviación estándar, los valores de grado de conversión muestran un gran aumento en la resina Ena comparado con el grupo control (63,81%), cuando es realizado pospolimerización con calor seco (89,02%) y una gran disminución cuando es realizado con agua en ebullición (36,41%). Con-clusiones: el proceso de curado posterior por microondas y autoclave aumenta los valores de microdureza y grado de conversión, y el agua destilada a temperaturas altas disminuye la microdureza de la superficie de las resinas compuestas
Objetive: to evaluate micro-hardness and conversion levels after different postcuring techniques in two types of composite resins. Materials and methods: 36 12mmdiameter 4 mm-height specimens were manufactured with two resins: Flitek z350 and Ena Miscerium. After the manufacturing, specimens were taken to the microduremeter and infrared spectroscopy, and endured four post-polymerization processes: boiling water, microwave, dry heat, autoclave and horno gradia. Results: statistical analyses (by Anova) of two factors with Tukey’s Post Hoc Test by evaluated resin was performed, there appear media and standard deviation, conversion level degrees show a large increase in Ena resin compared to the control group (63.81%) when dry heat post-polymerization is performed (89.02%) and a large decrease when it is performed with boiling water (36.41%).Conclusions: the post-curing process by microwave and autoclave increase micro-hardness level and conversion level, while distilled water at high temperatures diminishes superficial micro-hardness of composite resins.
Objetivo: avaliar a microdureza e o grau de conversão depois de diferentes técnicas pós-curado em dois tipos de resinas compostas. Materiais e métodos: realizaram-se 36 corpos de teste com 12 mm de diâmetros e 4 mm de altura, com duas resinas: Filtek z350 e Ena Miscerium. Depois da confecção os corpos de teste foram levados ao microdurômetro e a espectroscopia de infravermelho, e submetidos a quatro processos de pós-polimerização: água em ebulição, micro-onda, calor seco, autoclave e Horno Gradia. Resultados: realizouse análise estatística mediante de Anova de dois fatores com pós-teste de Tukey por resina avaliada, apresentam-se média e desvio padrão, os valores de grau de conversão evidenciam um grande aumento na resina Ena comparado com o grupo controle (63,81%), quando realizado pós-polimerização com calor seco (89,02%) e uma grande diminuição quando realizado com água em ebulição (36,41%). Conclusões: o processo de curado posterior por micro-ondas e autoclave aumenta os valores de microdureza e grau de conversão, e a água destilada a temperaturas altas diminui a microdureza da superfície das resinas compostas.
Publisher: Universidad Cooperativa de Colombia
Appears in Collections:Revista Nacional de Odontología

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.